ABSTRACT:
A study was made of the processing of 6-mm-thick AA 6061 plates using friction-stir processing. A plan of experiments was prepared based on the abilities of a universal milling machine, where the tool-rotation speed varied from 900 r/min to 1400 r/min, the processing speed from 31.5 mm/min to 45 mm/min and the tool tilt angle was held constant at 1.5°. Samples for Vickers micro-hardness measurements and special miniature tensile-testing were prepared. A set of optimal processing parameters was determined at which quality welds can be made with a minimal increase in the weld hardness and in the tensile strength.
Cite this article:
K. Nagaraju, A. Devaraju, B. Manichandra. Mechanical Characterization of Al 6061 Surface Composite with Nano particles (TiC) Fabricated by Friction Stir Processing. Research J. Engineering and Tech. 2018;9(4): 288-292. doi: 10.5958/2321-581X.2018.00038.7
Cite(Electronic):
K. Nagaraju, A. Devaraju, B. Manichandra. Mechanical Characterization of Al 6061 Surface Composite with Nano particles (TiC) Fabricated by Friction Stir Processing. Research J. Engineering and Tech. 2018;9(4): 288-292. doi: 10.5958/2321-581X.2018.00038.7 Available on: https://www.ijersonline.org/AbstractView.aspx?PID=2018-9-4-2